Inshine P602
Product Features
A high cut-off ultraviolet POE. With low water vapor permeability and high volume resistivity. The safety and long-term aging resistance of components operating in high temperature and humidity environments.
Product characteristics
|
Test items |
unit |
Referenced standards |
Specification value |
|
|
Wide in width |
mm |
GB/T 13542.2-2009 |
standard value（0-+5） |
|
|
Thickness |
mm |
GB/T 13542.2-2009 |
0.45-0.65 |
|
|
Tensile strength（MD） |
MPa |
GB/T 13542.2-2009 |
≥6 |
|
|
Tensile strength（TD） |
MPa |
GB/T 13542.2-2009 |
≥6 |
|
|
Elongation at break（MD） |
% |
GB/T 13542.2-2009 |
≥600 |
|
|
Elongation at break（TD） |
% |
GB/T 13542.2-2009 |
≥600 |
|
|
Heat shrinkage rate（120℃×3min）MD |
% |
GB/T 13542.2-2009 |
≤3.0 |
|
|
Heat shrinkage rate（120℃×3min）TD |
% |
GB/T 13542.2-2009 |
≤0.5 |
|
|
POE and backboard peel strength |
N/cm |
GB/T 2790-1995 |
≥60 |
|
|
POE and glass peel strength |
N/cm |
GB/T 2790-1995 |
≥80 |
|
|
Transmittance（380-1100nm） |
% |
T/CPIA0004-2017 |
≥90 |
|
|
Transmittance（380-290nm） |
% |
T/CPIA0004-2017 |
≤30 |
|
|
Volume resistivity |
Ω·cm |
GB/T 1410-2006 |
≥1×1016 |
|
|
Breakdown voltage intensity (AC method) |
KV/mm |
GB/T 1408.1-2016 |
≥28 |
|
|
CTI |
V |
GB/T 4207-2012 |
≥600 |
|
|
Crosslinking degree (xylene method) |
% |
GB/T 29848-2013 |
75-95 |
|
|
Surface roughness |
μm |
GB/T 1031-2009 |
Ra（min）＞10 |
|
|
Haze (after crosslinking) |
-- |
ISO 14782:1999 |
≤5.0 |
|
|
Water vapor transmission rate 38 ℃ × 90% RH |
g/(m2·day) |
GB/T 26253-2010 |
≤5.0 |
|
|
Anti PID performance (85 ℃ × 85% RH × 192H) |
% |
IEC TS62804:2015 |
≤3% |
|
|
Creep performance (after crosslinking) |
% |
GB/T 11546.1-2008 |
130℃烘箱内1H经受0.005MPa应力后蠕变率≤10% |
|
|
Constant damp heat test 85℃×85%RH 1000H |
Yellowing index△YI |
-- |
IEC 61215-2 2016 |
≤3.0 |
|
Peel strength with glass |
N/cm |
≥40 |
||
|
UV aging resistance test 120KWH/m2 |
Yellowing index△YI |
-- |
IEC 61215-2 2016 |
≤3.0 |
|
Peel strength with glass |
N/cm |
≥40 |
||